Hydrophilic, high protein binding, low fluorescence, western blotting membrane

ABSTRACT

Hydrophilic membrane particularly suited for blotting applications, preferably Western blotting. A pre-wet hydrophobic membrane substrate, preferably made of PVDF, is contacted with a monomer solution and subjected to a UV-initiated free radical polymerization step to render the substrate permanently hydrophilic. The resulting membrane exhibits low background fluorescence, high protein binding, excellent retention of protein sample spot morphology, and extended dynamic range (high signal-to-noise ratio, enhanced sample detectability). The membrane demonstrates comparable or higher performance in Western blotting applications than conventional nitrocellulose Western blotting membranes, particularly for protein detection at low sample concentrations, and is directly water-wettable, eliminating the need for an alcohol pre-wet step prior to use.

This application claims priority of Provisional Application Ser. No. 61/189,302 filed Aug. 18, 2008, the disclosure of which is hereby incorporated by reference.

BACKGROUND OF THE INVENTION

“Blotting” or “electro-blotting” refers to the process used to transfer biological samples from a gel to a membrane under the influence of an electric field. The process requires a membrane that can immobilize biomolecular samples for subsequent detection. This places specific requirements on the membranes related to surface area, porosity, and protein binding capacity.

Western blotting is one modification of this technique that involves the immobilization of proteins on membranes before detection using monoclonal or polyclonal antibodies. Prior to protein immobilization on the membrane, sample proteins are separated using SDS polyacrylamide gel electrophoresis (SDS-PAGE) to separate native or denatured proteins. The proteins are then transferred or electro-blotted onto a membrane, where they are probed and ultimately detected using antibodies specific to a target protein. Western blotting membranes are typically made of nitrocellulose (NC) or polyvinylidene fluoride (PVDF). The specificity of the antibody-antigen interaction can enable a single protein to be identified among a complex protein mixture.

To summarize, Western blotting involves application of a protein sample (lysate) onto a polyacrylamide gel, subsequent separation of said complex mixture by electrophoresis, and transferal or “electro-blotting” of separated proteins onto a second matrix, generally a nitrocellulose or polyvinylidene fluoride (PVDF) membrane. Following the transfer, the membrane is “blocked” to prevent nonspecific binding of antibodies to the membrane surface. Many antibody labeling or tagging strategies are known to those skilled in the art. In the simplest protocols, the transferred proteins are incubated or complexed with a primary enzyme-labeled antibody that serves as a probe. After blocking non-specific binding sites a suitable substrate is added to complex with the enzyme, and together they react to form chromogenic, chemiluminescent, or fluorogenic detectable products that allow for visual, chemiluminescence, or fluorescence detection, respectively. The most sensitive detection schemes make use of chemiluminescent or fluorescent phenomena. In chemiluminescent detection, an enzyme-substrate complex produces detectable optical emissions (chemiluminescence). These emissions are recorded and measured using suitable detectors such as film or photonic devices. Absence or presence of signal indicates whether a specific protein is present in the lysate, and signal intensity is related to the level of the protein of interest, which in some cases may be quantifiable.

The use of nitrocellulose membranes is ubiquitous in immunodetection assay work, particularly in Western blotting. This is partially due to historical considerations, and partially due to ease of use. Nitrocellulose blotting membranes do not require an organic liquid pre-wet step, a requirement for working with hydrophobic membranes. Hydrophobic membranes require an alcohol pre-wet step followed by a water exchange step (for alcohol removal), before assembly within the blot-transfer assembly. Intrinsically hydrophobic membranes afford a limited time-frame for this assembly; the potential for the membrane to dry out is significant. Once dry, the membrane cannot be re-wet unless the pre-wet sequence is repeated. Once the membrane is contacted to the gel, removal prior to transfer can effectively ruin the gel and the separated protein samples contained. The pre-wet step is time consuming and can considerably impede workflow. A hydrophilic membrane will remain wet for a longer time interval, and can be re-wet with water if it does dry out before assembly.

Nitrocellulose blotting membranes are water wet-able and show satisfactory performance for most blotting applications. But nitrocellulose is not as mechanically or chemically stable as PVDF. PVDF will maintain its mechanical integrity over a long timeframe, whereas NC will become brittle and discolored. PVDF membrane blots can be stripped of antibodies and be re-probed. NC blots cannot. NC is prone to air oxidation, wherein it can become hazardous. It requires a separate waste stream, and when disposed of must be damped with a wetting agent, usually water.

Hydrophobic PVDF blotting membranes possess equivalent protein binding ability to NC blotting membranes, but exhibit superior blotting performance. Much lower sample concentrations can be detected under the same conditions on these PVDF membranes compared to NC. Low-background fluorescence hydrophobic PVDF blotting membranes exhibit the same enhanced sample detection while enabling the use of fluorescent detection schemes.

It therefore would be desirable to provide a hydrophilic PVDF membrane for immunodetection assays such as Western blotting, with performance characteristics that approach the lower sample detection limits and low background fluorescence that are characteristic of hydrophobic PVDF membranes. This invention addresses these requirements.

SUMMARY OF THE INVENTION

Those skilled in the art of surface modification for the purpose of altering substrate surface energies, and in particular with regard to surfaces intended for contact with biological systems, will concur that hydrophilic surface modifications traditionally exhibit low protein binding behavior. The embodiments disclosed herein build on the serendipitous and unexpected discovery that space polymers derived from certain monomeric acrylamide mixtures, and formed using free-radical polymerization reactions, can give rise to surface modifications that are not only hydrophilic, but also demonstrate a high level of protein binding.

Much of the prior art describes the use of hydroxyl containing monomers, usually carbonyl ester containing acrylate polymers, to produce membrane surface modifications having hydrophilic character and high resistance to protein binding. However, it is known that polymers from such monomers are not resistant to strong alkaline solutions. For example, a solution of 1.0 normal sodium hydroxide will hydrolyze the carbonyl containing acrylate polymers to acrylic acid containing polymers. Such acrylic acid containing polymers are ionically charged under certain pH conditions, and will attract and bind oppositely charged proteins or biomolecules, thus increasing sorption and membrane fouling. In addition, acrylic acid containing polymers swell in water to an extent that they constrict pore passages, thus reducing membrane permeability and productivity. Moreover, polymers from hydroxyl containing monomers, such as hydroxy acrylates, further react in strong alkaline solutions and degrade into soluble low molecular weight fragments, which dissolve away and expose the underlying substrate porous media or membrane.

Practitioners attempting to develop optimized membranes either for filtration or non-filtration applications in the pharmaceutical and biotechnology industries must overcome significant problems. Facing stringent cost, performance and safety requirements, a practitioner must use materials and develop manufacturing methods that produce membranes with not only optimized flow and retention characteristics, but be economical to produce, meet cleanliness criteria, be stable to the various chemical environments which are commonly encountered, and be very either very resistant to biomolecule adsorption, or very strongly adsorbing, depending upon the intended end-use. Thus, in this instance, it is very desirable to have a membrane modification that results in a hydrophilic, biomolecule adsorptive surface that is heat stable, which is resistant to degradation by any potential reagent solutions, and which has very low levels of material capable of being extracted there-from.

Protein binding results from early investigations into mixed-acrylamide polymeric surface modifications indicated that certain mixtures of hydrophilic bis-acrylamide crosslinking monomers and monofunctional neutral or charged acrylamides can, when copolymerized using UV-initiated or electron beam-initiated free-radical techniques, produce high protein-binding hydrophilic surface modifications. However, initial starting levels of each monomer had to be severely decreased before observing satisfactory dot blot morphology and blotting transfer performance.

The problems of the prior art have been overcome by the present embodiments, which provide a hydrophilic membrane particularly suited for blotting applications, preferably Western blotting. More specifically, a pre-wet hydrophobic membrane substrate, preferably made of PVDF, is contacted with a monomer solution and subjected to polymerizing conditions to render the substrate permanently hydrophilic.

The resulting membrane exhibits low background fluorescence, high protein binding, excellent retention of protein sample spot morphology, and extended dynamic range (high signal-to-noise ratio, enhanced sample detectability). Where chemiluminescence is used for detection, the level of background fluorescence inherent in the unmodified parent membrane is not as critical. The membrane demonstrates comparable or higher performance in Western blotting applications than conventional nitrocellulose blotting membranes, particularly for detection at low sample concentrations, and is directly water-wettable, eliminating the need for an alcohol pre-wet step prior to use. The membrane exhibits complete, instant, and uniform wetting upon contact with water, and exhibits delayed wetting when contacted with a saturated aqueous aluminum chloride solution. That is, when said membrane is placed on the surface of this saturated aqueous aluminum chloride solution, it wets through in a minimum time interval of not less than 1 second).

BRIEF DESCRIPTION OF THE DRAWINGS

FIGS. 1-3 are diagrams of Western blot results using treated membranes in accordance with certain embodiments.

DETAILED DESCRIPTION

The membranes hydrophilically modified in accordance with embodiments of the present disclosure provide immunodetection assay platforms that are comparable to, or exhibit superior blotting performance to nitrocellulose membranes, particularly with respect to expansion of the low end of the dynamic range of sample detectability. For example, in FIG. 1, Western blotting results from a typical development run demonstrate the performance differences between the hydrophilic PVDF blotting membrane of this invention, and the controls (FL—hydrophobic PVDF membrane, and NC—Whatman/S&S BA-85 membrane). Each horizontal strip in the figure contains 5 separate Western transfer blots; three blots on hydrophilic PVDF development samples, and one blot on each of the control membranes. Each horizontal strip of 5 Western blots is the result from one electrophoresis and transfer experiment (5 gels followed by 5 blots were run in each experiment). By design, each experiment embodies identical conditions on each gel/blot with identical quantities of protein sample (applied in 4 lanes across each gel) before electrophoresis and transfer. The results shown are the recorded (chemiluminescent) transfer blots for the detection of 2 proteins (HSP70 and GAPDH) from a complex sample mixture (lysate), applied at decreasing sample concentrations, from left-to-right on each gel, and corresponding to: 5 ug, 2.5 ug, 1.25 ug, 0.67 ug.

Suitable porous membranes include those formed from aromatic sulfone polymers, polytetrafluoroethylene, perfluorinated thermoplastic polymers, polyolefin polymers, ultrahigh molecular weight polyethylene, polyamides including Nylon 6 and Nylon 66, and polyvinylidene fluoride, with polyvinylidene fluoride being particularly preferred. Porous membranes include both microporous membranes and ultrafiltration membranes, and are preferably in the form of sheets. Generally the average pore sizes include those between 0.001 and 10 microns. Blotting membranes are nominally 0.45 um pore size materials. Preferred starting membranes have a porosity (void volume) range specification of 68-73%. Blotting membranes are traditionally symmetric. However, the coating could be applied to an asymmetric membrane.

The polymeric coating can be a copolymer or terpolymer formed from at least one polyfunctional monomer modified with at least one hydrophilic functional group, said hydrophilic polyfunctional monomer(s) selected from the group consisting of polyfunctional acrylamides, polyfunctional methacrylamides and diacroylpiperazines, and formed from at least one monofunctional monomer modified with at least one hydrophilic functional group, said hydrophilic monofunctional monomer(s) selected from the group consisting of monofunctional acrylamides, monofunctional methacrylamides, and acryloyl piperazines.

It was found that a porous hydrophobic membrane, preferably one made of polyvinylidene fluoride coated with a crosslinked acrylamide-methylene-bis-acrylamide copolymer was rendered highly hydrophilic. Furthermore, at the copolymer level that was applied to the porous PVDF membrane samples in early iterations of this invention, IgG binding assays revealed protein binding levels to be in the neighborhood of 400 ug/cm². This level is typical of the parent hydrophobic PVDF membrane and of conventional nitrocellulose membranes. The first surprising result was that membranes so prepared were both hydrophilic, and high protein-binding. However, the Western blotting performance of these initial samples (those that exhibited this high level of protein binding) was not satisfactory in terms of maintaining small sample blot size (blot morphology), and in terms of sample capture in blot transfers. By modifying the copolymer coating level, satisfactory blotting performance was realized. At these modified levels, protein binding levels were reduced to between 250 and 325(00) ug/cm², but Western blotting performance rose to levels intermediate between nitrocellulose and the preferred parent hydrophobic PVDF membrane. Surprisingly, the present inventors found that the protein binding level is not the best or only predictor of Western blotting membrane performance. Sacrificing some protein binding ability by modifying the coating level on the substrate can result in improved blotting performance.

Thus, component levels and relative concentrations of the modifying formulation are critical to obtain acceptable immunodetection assay performance. A low overall solids concentration in a highly specific component ratio balances water-wetting performance against blotting performance. The very low background fluorescence level of the substrate membrane is preserved. If, however, the level of surface modification chemistry is too low, the result is a membrane that is not water-wettable to an acceptable extent. If the level of surface modification is too high the resulting membranes exhibit extremely high surface energies. As stated earlier, at higher levels of surface modifying chemistry, the measured protein binding capacity is roughly equivalent to nitrocellulose and hydrophobic PVDF membranes, but poor electro-blotting performance results.

In accordance with certain embodiments, the total solids level in the modifying/reactant solution is to be adjusted to between 0.90% and 1.10% by weight. A total solids concentration in this range with the specified component ratio results in optimal blotting performance. This formulation includes a UV-photoinitiator component.

Suitable amounts of the acrylamide monofunctional monomer and the bis-acrylamide crosslinking monomer in the reactant solution are to be between 0.20% and 2.00% by weight (each), preferably with amounts between 0.30% and 0.60% by weight (each), and most preferably between 0.40% and 0.50% by weight (inclusive, each). The preferred ratio of acrylamide to bis-acrylamide of the monomer reactant solution is about 1:1 (mass/mass). The preferred overall monomer concentration of acrylamide:methylene-bis-acrylamide monomer reactant solution is between 0.5% and 1.5% by mass. A suitable UV-photoinitiator component is present in 0.01% to 0.20% by weight preferably between 0.05 and 0.15% by weight, and most preferably between 0.09% and 0.11%, by weight. Suitable UV-photoinitiators include IRGACURE® 2959 (2-hydroxyl-1-[4-(2-hydroxyethoxy)phenyl]-2-methyl-1-propanone (Ciba-geigy) 500, 754, 2959, and 819DW. Methods for preparation of the modified porous membrane substrate in accordance with certain embodiments include the steps of providing a porous membrane substrate, contacting the surface of the porous membrane substrate with a reactant solution comprising acrylamide and methylene-bis-acrylamide, and a suitable photoinitiator, removing the membrane from the solution, and polymerizing the coating in situ on the membrane substrate by exposing the same to radiation of a suitable wavelength and intensity for a suitable time interval. Preferably the porous membrane contacted with the reaction solution is irradiated with an ultraviolet light source. Filters may be used to reduce or eliminate undesirable wavelengths which may cause damage to the porous membrane. The amount of exposure time to the UV light and the intensity thereof should be familiar to those skilled in the art.

In the preferred embodiment of the invention, a laboratory-scale preparation of the reactant monomer solution is made by dissolving 1.00 g acrylamide, [H₂C═CH—C(O)—NH₂] monofunctional monomer; 0.80 g methylene-bis-acrylamide, [H₂C(—NH—C(O)CH═CH₂)₂] cross-linking monomer; and, 0.20 g Irgacure 2959 photo-initiator into 198.00 g of Milli-Q® water. An extended mixing interval of about 2 hours is required to fully dissolve the cross-linker and the photo-initiator.

More specifically, the porous hydrophobic starting membrane is pre-wet by immersion in an organic liquid or in an aqueous solution thereof that does not swell or dissolve the porous membrane, and which pre-wets the entire porous surface of the membrane.

The liquid may be a low molecular weight alcohol, or a mixture of water and a miscible organic liquid. Suitable liquids or compositions include methanol, ethanol, isopropanol, water mixtures thereof, acetone/water mixtures, and tetrahydrofuran/water mixtures of sufficiently low surface tension to affect wetting the entire membrane surface.

The purpose of this pre-wetting step is to assure that the entire membrane surface is rendered wettable by water, and subsequently by the aqueous reactant monomer solution. The pre-wetting step must be followed by a rigorous exchange step with water to eliminate the presence of the organic solvent. These pre-wetting solvents or water mixtures thereof can exert a negative influence upon the intended polymerization of the reactant monomers.

Subsequent immersion and gentle agitation of the water-wet porous membrane in the reactant solution allows the entire surface of the porous membrane to be wet with reactant solution. As long as excess water is removed from the membrane prior to immersion in the reactant solution, no significant dilution of the reactant solution will occur.

The sample is withdrawn after a short (two minute) time interval and excess reactant solution is removed from the membrane sample. The reactant solution-wetted membrane is anaerobically exposed to UV radiation to effect the polymerization directly onto the entire porous membrane surface. The resulting coated membrane exhibits: Immediate, complete, and thoroughly uniform wetting when contacted onto a water surface; A high level of Western blotting performance; A high level of protein binding (≧250 ug/cm² IgG) by radio-labeled assay; and, Low background fluorescence (about 2000 rfu @ 485 nm/535 nm excitation/emission wavelengths using a TECAN GENios FL fluorescence reader with detector gain set at 86, and running Magellan 5.0 software package), which is about twice the background fluorescence of the untreated (unmodified parent hydrophobic) membrane under the same measurement conditions. When placed on the surface of a saturated aqueous aluminum chloride solution, the membrane will wet through in a minimum time interval of not less than 1 second, and in a maximum time interval that may exceed 60 seconds.

EXAMPLE 1

Commercially available hydrophobic PVDF membrane from Millipore Corporation (IPFL00000) was immersed in methyl alcohol. The membrane was withdrawn and immersed in water with agitation to extract methanol for 1 minute. The membrane was withdrawn and immersed in fresh water for an additional 2-minute interval and then placed in fresh water before immersion in reactant monomer solution. Excess water was drained from the membrane and the membrane was then immersed in monomer reactant solution with gentle agitation for 2 minutes. Membrane was then exposed to UV radiation from both sides in a UV curing process at a line speed of 15 to 25 fpm. Membrane was recovered and placed into a water bath to remove unreacted monomer and non-adhering oligomers and polymer. Samples were dried either in air at room temperature overnight, or in a static forced-air oven between 60° C. and 80° C. for 10 minutes, or on an impingement dryer at 90-110° C. at a line speed of 15 to 25 fpm. Average membrane extractables as determined by an in-house TOC (Total Organic Carbon) method were measured to be about 1.44 ug/cm2, as shown in Table 1.

TABLE 1 Total Organic Carbon (TOC) - Five (5) 47 mm disks. Requestor ID: ML6UJP37 Requestor: Antoni Peters PVDF Hydrophillic IPFL Membrane Received For Blotting and Immuno Assays Applications Ext. for TOC Analysis Extraction By: A. Pervez TOC By: M. Santos-Rosa & A. Pervez Date: Oct. 16-19, 2006 Ext. Temp. Ext. Time Ext. Vol. Ext. Area Ext. Solvent [° C.] [Hours] [g] [cm 2] MilliQ Water Ambient 24 40 86.75 Summary Results TOC Acid/Oxid TOC Corrected TOC TOC TOC Sample ID [μL/min] [ppm C] [ppm C] [μg C] [μg C/cm 2] Water Blank 0.20/0.20 0.0639 T102 072806 A: -MBAM/AC/I-2959 0.75/1.00 3.29 3.23 129 1.49 T102 072806 B: -MBAM/AC/I-2959 0.75/1.00 2.91 2.85 114 1.31 T102 072806 C: -MBAM/AC/I-2959 0.75/1.00 3.33 3.27 131 1.51

Average extractable residual monomer levels were determined by HPLC. Values determined from 3 samples are provided in Table 2.

TABLE 2 Extractable Monomer Levels by HPLC - Same samples as shown in Table 1. Acrylamide MBAM Irgacure(R) 2959 Sample (μg/cm2) (μg/cm2) (μg/cm2) T102 072806A 0.002 0.105 N.D. T102 072806B 0.005 0.091 N.D. T102 072806C 0.011 0.094 N.D.

EXAMPLE 2

The procedure of Example 1 was used to treat PVDF membranes having the specifications, treatment conditions and reactant solutions shown in Tables 3A-D, 4A-D, and 5A-D.

TABLE 3A MODIFICATION DATA for Hydrophilic PVDF Western Blotting Membrane Membrane Monomer Starting Casting Starting Membrane Properties Mix Membrane Dryer Flow Time Roll No. Lot# Lot Data Temperature (F.) Thick (um) Porosity (%) Bbl Pt (psi) (seconds) RUN R - No Mix Ajustment - Footage VS Monomer Mix Concentration NA NA NA NA NA NA NA NA R01 R Mix 1 IPFL 071007 T214 300 112 72.8 9.4 56.0 R02 R Mix 1 IPFL 071007 T205 300 113 73.0 9.4 63.0 R03 R Mix 1 IPFL 071007 T205 300 113 73.0 9.4 63.0 R04 R Mix 1 IPFL 071007 T205 300 113 73.0 9.4 63.0 R05 R Mix 1 IPFL 071007 T205 300 113 73.0 9.4 63.0 R06 R Mix 1 IPFL 071007 T206 300 111 72.4 9.5 65.0 R07 R Mix 1 IPFL 071007 T206 300 111 72.4 9.5 65.0 R08 R Mix 1 IPFL 071007 T206 300 111 72.4 9.5 65.0 R09 R Mix 1 IPFL 071007 T206 300 111 72.4 9.5 65.0 R10 R Mix 1 IPFL 071007 T214 300 112 72.8 9.4 56.0 R11 R Mix 1 IPFL 071007 T214 300 112 72.8 9.4 56.0 R12 R Mix 1 IPFL 071007 T214 300 112 72.8 9.4 56.0 R12 End NA NA 300 NA NA NA NA

TABLE 3B MODIFICATION DATA for Hydrophilic PVDF Western Blotting Membrane Monomer Mix Component Concentrations Actual Actual Actual Actual Totalized Monomer Mix AC MBAM I-2959 Total Solids Footage Roll No. Sample ID Wt % (HPLC) Wt % (HPLC) Wt % (HPLC) Wt % (HPLC) By Roll RUN R - No Mix Ajustment - Footage VS Monomer Mix Concentration NA R Mix 1 DRUM 0.5156 0.4214 0.1130 1.0500 0 R01 MM1 Start 0.5091 0.4042 0.1102 1.0235 0 R02 MM2 0.5105 0.3957 0.1094 1.0156 500 R03 MM3 0.5038 0.3837 0.1055 0.9931 800 R04 MM4 0.4996 0.3773 0.1001 0.9771 1100 R05 MM5 0.4948 0.3708 0.0999 0.9655 1250 R06 MM6 0.4935 0.3685 0.1020 0.9640 1550 R07 MM7 0.4868 0.3618 0.0995 0.9481 1850 R08 MM8 0.4868 0.3605 0.0974 0.9448 2150 R09 MM9 0.4777 0.3553 0.0956 0.9286 2300 R10 MM10 0.4721 0.3528 0.0956 0.9204 2600 R11 MM11 0.4673 0.3521 0.0932 0.9125 2900 R12 MM12 0.4682 0.3561 0.0918 0.9161 3200 R12 End MM13 End 0.4574 0.3546 0.0879 0.8999 3300

TABLE 3C MODIFICATION DATA for Hydrophilic PVDF Western Blotting Membrane Nip Nip UV Chamber Conditions Aisle Wall Line N₂ Flow Starting Press Press Speed Lamps Lamps Top/Bottom UV P1 UV P3 UV P2 O₂ Level Roll No. psi psi ft/min Type/No Config (SCFM) Inch HWC Inch HWC Inch HWC (ppm) RUN R - No Mix Ajustment - Footage VS Monomer Mix Concentration NA NA NA NA NA NA NA 1.0 1.6 1.0 90.0 R01 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 70.0 R02 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 56.7 R03 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 39.3 R04 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 33.0 R05 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 28.8 R06 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 27.8 R07 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 26.9 R08 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 26.4 R09 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 27.4 R10 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 25.2 R11 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 27.1 R12 20 20 20 H/4 Staggered 10/9.5 1.1 1.7 1.1 27.8 R12 End NA NA NA NA NA NA 1.1 1.7 1.1 25.2

TABLE 3D MODIFICATION DATA for Hydrophilic PVDF Western Blotting Membrane Water Wet Water Wet Water Wet Salt Wet Salt Wet Salt Wet Salt Wet Fluores QC Blotting Western Speed Uniform Through Time Time Time Time BKG Pass/Fail Blotting Roll No. OK? X-web? OK? Seconds Seconds Seconds Seconds RFU Control Live Lysate RUN R - No Mix Ajustment - Footage VS Monomer Mix Concentration NA NA NA NA NA NA NA NA NA NA ≧NC R01 Y Y Y 4.7 3.5 3.0 3.7 1750.57 Pass 9 Band ≧NC R02 Y Y Y 1.4 2.4 2.4 2.1 N/Avail. N/Avail. ≧NC R03 Y Y Y 1.4 2.4 2.4 2.1 N/Avail. N/Avail. ≧NC R04 Y Y Y 2.1 2.2 2.5 2.3 N/Avail. N/Avail. ≧NC R05 Y Y Y 2.9 3.1 2.9 3.0 2015.63 Pass 9 Band ≧NC R06 Y Y Y 2.2 2.3 2.3 2.3 N/Avail. N/Avail. ≧NC R07 Y Y Y 4.1 3.9 4.0 4.0 N/Avail. N/Avail. ≧NC R08 Y Y Y 2.3 3.7 3.2 3.1 N/Avail. N/Avail. ≧NC R09 Y Y Y 5.7 7.3 5.3 6.1 1927.95 Pass 9 Band ≧NC R10 Y Y Y 5.4 7.1 5.4 6.0 N/Avail. N/Avail. ≧NC R11 Y Y Y 6.3 7.5 5.6 6.5 N/Avail. N/Avail. ≧NC R12 Y Y Y 8.5 7.8 7.6 8.0 1708.5  Pass 9 Band ≧NC R12 End Y Y Y 16.7 16.5 16.3 16.5 NA NA ≧NC

TABLE 4A MEMBRANE MODIFICATION DATA - Hydrophilic PVDF Western Blotting Membrane Heat Treat Temperature Membrane Monomer Starting or Mod Line Casting Run Mix Membrane Dryer Dryer Segment Roll No. Lot# Lot Data Temperature Temperature RUN S - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED NA NA NA NA Test R01 S Mix 1 IPFL 071007 T203 205 300 S1 R02 S Mix 1 IPX 070907 R103 205 300 S1 R03 S Mix 1 IPX 091407 T103 205 310 S1 R04 S Mix 1 IPX 120307 T107 205 300 S1 R05 S Mix 1 IPX 091407 T102 205 310 S1 R06 S Mix 1 IPX 070907 R105 204 300 S2 R07 S Mix 1 IPX 120307 T107 200 300 S2 R08 S Mix 1 IPX 120307 T107 Transition 300 S2 R09 S Mix 1 IPX 120307 T107 205 300 S2 R10 S Mix 1 IPX 120307 T107 Transition 300 S2 R11 S Mix 1 IPX 120307 T107 210 300 S2 R12 S Mix 1 IPX 120307 T107 210 300 S2 R13 S Mix 1 IPX 120307 T107 210 300 Segment 1 Variation of starting membrane properties Segment 2 Variation of line speed and dryer temperature

TABLE 4B MEMBRANE MODIFICATION DATA - Hydrophilic PVDF Western Blotting Membrane Monomer Mix Samples and Mix Component Concentrations Monomer Actual Actual Actual Actual Starting Membrane Properties Mix AC MBAM I-2959 Total Solids Totalized Run Roll Thick Porosity Bbl Pt Flow Time Sample Wt % Wt % Wt % Wt % Footage Segment No. (um) (%) (psi) (seconds) ID (HPLC) (HPLC) (HPLC) (HPLC) By Roll RUN S - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED NA NA NA NA NA NA MM1B 0.4979 0.3894 0.1005 0.9878 150 Test R01 112 72.8 9.6 61.0 MM1C start 0.4926 0.3877 0.1005 0.9808 300 S1 R02 115 74.8 9.3 55.0 MM2B 0.4893 0.3849 0.0996 0.9738 450 S1 R03 115 66.4 9.6 59.0 MM3B 0.4812 0.3785 0.0971 0.9568 600 S1 R04 126 72.9 9.4 65.0 MM4B 0.4780 0.3760 0.0963 0.9503 750 S1 R05 122 66.2 11.1 78.3 MM5B 0.4761 0.3733 0.0954 0.9448 950 S1 R06 130 74.7 10.7 74.0 MM6B 0.4785 0.3757 0.0953 0.9495 1100 S2 R07 126 72.9 9.4 65.0 MM7B 0.4699 0.3678 0.0934 0.9311 1200 S2 R08 126 72.9 9.4 65.0 MM8B 0.4673 0.3656 0.0926 0.9255 1305 S2 R09 126 72.9 9.4 65.0 MM9B 0.4660 0.3644 0.0925 0.9229 1405 S2 R10 126 72.9 9.4 65.0 MM10B 0.4655 0.3637 0.0917 0.9209 1505 S2 R11 126 72.9 9.4 65.0 MM11B 0.4642 0.3619 0.0910 0.9171 1605 S2 R12 126 72.9 9.4 65.0 MM12B 0.4618 0.3598 0.0903 0.9119 1705 S2 R13 126 72.9 9.4 65.0 MM13B Not Not Not Not 1855 Available Available Available Available Segment 1 Variation of starting membrane properties Segment 2 Variation of line speed and dryer temperature

TABLE 4C MEMBRANE MODIFICATION DATA - Hydrophilic PVDF Western Blotting Membrane Nip Nip UV Chamber Conditions Aisle Wall Line N₂ Flow Starting Run Press Press Speed Top/Bottom UV P1 UV P3 UV P2 O₂ Level Segment Roll No. psi psi ft/min (SCFM) Inch HWC Inch HWC Inch HWC (ppm) RUN S - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED NA NA NA NA NA NA NA NA NA NA Test R01 20 20 20 10/9.5 1.0 1.5 1.1 15.0 S1 R02 20 20 20 10/9.5 1.0 1.5 1.1 42.0 S1 R03 20 20 20 10/9.5 1.0 1.5 1.1 40.0 S1 R04 20 20 20 10/9.5 1.0 1.5 1.1 40.0 S1 R05 20 20 20 10/9.5 1.0 1.5 1.1 40.0 S1 R06 20 20 20 10/9.5 1.0 1.5 1.1 40.0 S2 R07 20 20 22 10/9.5 1.0 1.4 1.1 53.7 S2 R08 20 20 20 10/9.5 1.0 1.4 1.1 39.1 S2 R09 20 20 20 10/9.5 1.0 1.4 1.1 37.6 S2 R10 20 20 18 10/9.5 1.0 1.4 1.1 33.0 S2 R11 20 20 18 10/9.5 1.0 1.4 1.1 30.5 S2 R12 20 20 20 10/9.5 1.0 1.4 1.1 24.9 S2 R13 20 20 25 10/9.5 1.0 1.4 1.1 25.2 Segment 1 Variation of starting membrane properties Segment 2 Variation of line speed and dryer temperature

TABLE 4D MEMBRANE MODIFICATION DATA - Hydrophilic PVDF Western Blotting Membrane Water Wet Water Wet Water Wet Salt Wet Salt Wet Salt Wet Salt Wet Fluores QC Blotting Western Run Roll Speed Uniform Through Time Time Time Time BKG Pass/Fail Blotting Segment No. OK? X-web? OK? Seconds Seconds Seconds Seconds RFU Control Live Lysate RUN S - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED NA NA NA NA NA NA NA NA NA NA NA NA Test R01 Y Y Y     8.2 8.8 4.9 7.3 N/Avail. N/Avail. ≧NC S1 R02 Y Y Y    26.2 15.2 5.3 15.6 N/Avail. N/Avail. ≧NC S1 R03 Y Y Y     4.2 4.2 2.9 3.8 N/Avail. N/Avail. ≧NC S1 R04 Y Y Y     5.4 13.6 10.3 9.8 N/Avail. N/Avail. ≧NC S1 R05 Y N N     7.8 4.6 5.7 6.0 N/Avail. N/Avail. ≧NC S1 R06 Y Y Y    12.7 8.0 9.9 10.2 N/Avail. N/Avail. ≧NC S2 R07 Y Y Y >120* 90.0 25.0 Meaningless N/Avail. N/Avail. ≧NC S2 R08 Y Y Y >120* >120 40.0 Meaningless N/Avail. N/Avail. ≧NC S2 R09 Y Y Y >120* >120 30.0 Meaningless N/Avail. N/Avail. ≧NC S2 R10 Y Y Y >120* >120 55.0 Meaningless N/Avail. N/Avail. ≧NC S2 R11 Y Y Y >120* >120 80.0 Meaningless N/Avail. N/Avail. ≧NC S2 R12 Y Y Y >120* >120 80.0 Meaningless N/Avail. N/Avail. ≧NC S2 R13 Y Y Y >120  >120 55.0 Meaningless N/Avail. N/Avail. ≧NC Segment 1 Variation of starting membrane properties Segment 2 Variation of line speed and dryer temperature

TABLE 5A MODIFICATION DATA FOR Hydrophilic PVDF Western Blotting Membrane Heat Treat Temperature Membrane Monomer Starting or Mod Line Casting Run Mix Membrane Good Dryer Dryer Segment Roll No. Lot# Lot Data Footage Temperature Temperature RUN T - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED 1 NA 010908M1DRUM 0 NA NA 1 NA 010908M1-MM1 Tank 0 NA NA 1 NA 010908M1-MM2 Tank Diluted 0 NA NA 1 R01 010908M1 IPVH 050107 T101B 155 200 1 R02 010908M1 IPFL 071007 T203 90 200 300 2 R03 010908M1 IPX 120307 T109 90 200 300 2 R04 010908M1 IPX 120307 T109 90 200 300 2 R05 010908M1 IPX 120307 T109 90 Transition 300 2 R06 010908M1 IPX 120307 T109 90 220 300 2 R07 010908M1 IPX 120307 T109 90 215 300 2 R08 010908M1 IPX 120307 T109 90 215 300 2 R09 010908M1 IPX 120307 T109 90 Transition 300 2 R10 010908M1 IPX 120307 T109 90 220 300 3 R11 010908M1 IPX 091407 T101 10 205.4 300 3 R12 010908M1 IPX 071007 T213 90 205.5 300 3 R13 010908M1 IPX 120307 T104 90 205.8 300 3 R14 010908M1 IPX 070907 T105 90 206.1 300 3 R15 010908M1 IPX 070907 R102 90 205 300 3 R16 010908M1 IPX 070907 R106 90 205 300 3 R17 010908M1 IPX 120307 R110 90 205 300 3 NA 010908M1 NA 0 205 Segment 1 Diagnostic Segment 2 Dryer Temperature & Linespeed Variation Segment 3 Porosity and Thickness Variation - Starting Membrane

TABLE 5B MODIFICATION DATA FOR Hydrophilic PVDF Western Blotting Membrane Monomer Mix Samples and Component Concentrations Actual Monomer Actual Actual Actual Total Starting Membrane Properties Mix AC MBAM I-2959 Solids Totalized Run Roll Thick Porosity Bbl Pt Flow Time Sample Wt % Wt % Wt % Wt % Footage Segment No. (um) (%) (psi) (seconds) ID (HPLC) (HPLC) (HPLC) (HPLC) By Roll RUN T - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED 1 NA NA NA NA NA DRUM 0.76 0.60 0.15 1.51 0 1 NA NA NA NA NA MM1 0.75 0.58 0.15 1.48 0 1 NA NA NA NA NA MM2 Start 0.51 0.40 0.10 1.00 0 1 R01 109-125 Not Not Not Not Taken NA NA NA NA 375 Available Available Available 1 R02 112 72.8 9.6 61.0 Not Taken NA NA NA NA 675 2 R03 120 71.0 9.5 63.0 MM3 0.50 0.39 0.10 0.99 775 2 R04 120 71.0 9.5 63.0 Not Taken NA NA NA NA 875 2 R05 120 71.0 9.5 63.0 Not Taken NA NA NA NA 975 2 R06 120 71.0 9.5 63.0 Not Taken NA NA NA NA 1075 2 R07 120 71.0 9.5 63.0 Not Taken NA NA NA NA 1175 2 R08 120 71.0 9.5 63.0 Not Taken NA NA NA NA 1275 2 R09 120 71.0 9.5 63.0 Not Taken NA NA NA NA 1375 2 R10 120 71.0 9.5 63.0 Not Taken NA NA NA NA 1675 3 R11 118 66.7 8.3 46.7 MM4 0.48 0.38 0.09 0.96 1775 3 R12 116 72.3 9.0 56.0 Not Taken NA NA NA NA 1875 3 R13 119 72.4 9.7 66.0 Not Taken NA NA NA NA 1975 3 R14 130 74.7 10.7 74.0 Not Taken NA NA NA NA 2075 3 R15 134 73.4 9.9 65.0 Not Taken NA NA NA NA 2175 3 R16 114 72.4 9.7 67.0 Not Taken NA NA NA NA 2275 3 R17 113 70.2 9.4 61.0 Not Taken NA NA NA NA 2375 3 NA NA NA NA NA MM5 0.47 0.37 0.09 0.94 2675 Segment 1 Diagnostic Segment 2 Dryer Temperature & Linespeed Variation Segment 3 Porosity and Thickness Variation - Starting Membrane

TABLE 5C MODIFICATION DATA FOR Hydrophilic PVDF Western Blotting Membrane Nip Nip UV Chamber Conditions Aisle Wall Line N₂ Flow Starting Run Press Press Speed Top/Bottom UV P1 UV P3 UV P2 O₂ Level Segment Roll No. psi psi ft/min (SCFM) Inch HWC Inch HWC Inch HWC (ppm) RUN T - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED 1 NA 20 20 NA NA NA NA NA NA 1 NA 20 20 NA NA NA NA NA NA 1 NA 20 20 NA NA NA NA NA NA 1 R01 20 20 18 10/9.5 0.9 1.4 1.0 52.0 1 R02 20 20 20 10/9.5 0.9 1.4 1.0 77.0 2 R03 20 20 22-20 10/9.5 0.9 1.4 1.0 78.0 2 R04 20 20 18 10/9.5 0.9 1.4 1.0 44.0 2 R05 20 20 18 10/9.5 0.9 1.4 1.0 32.0 2 R06 20 20 18 10/9.5 0.9 1.4 1.0 32.0 2 R07 20 20 22-20 10/9.5 0.9 1.4 1.0 30.0 2 R08 20 20 18 10/9.5 0.9 1.4 1.0 26.0 2 R09 20 20 18-20 10/9.5 0.9 1.4 1.0 20.0 2 R10 20 20 20 10/9.5 0.9 1.4 1.0 22.0 3 R11 20 20 20 10/9.5 0.9 1.4 1.0 38.0 3 R12 20 20 20 10/9.5 0.9 1.4 1.0 34.0 3 R13 20 20 20 10/9.5 0.9 1.4 1.0 41.0 3 R14 20 20 20 10/9.5 0.9 1.4 1.0 21.0 3 R15 20 20 20 10/9.5 0.9 1.4 1.0 21.0 3 R16 20 20 20 10/9.5 0.9 1.4 1.0 21.0 3 R17 20 20 20 10/9.5 0.9 1.4 1.0 21.0 3 NA NA NA NA NA NA NA NA NA Segment 1 Diagnostic Segment 2 Dryer Temperature & Linespeed Variation Segment 3 Porosity and Thickness Variation - Starting Membrane

TABLE 5D MODIFICATION DATA FOR Hydrophilic PVDF Western Blotting Membrane Water Water Water Opacity/ Salt Salt Salt Salt QC Western Wet Wet Wet Speckle Trans- Wet Wet Wet Wet Fluores Blotting Blotting Run Roll Speed Uniform Through Level lucence Time Time Time Time BKG Pass/Fail Live Segment No. OK? X-web? OK? OK? OK? Seconds Seconds Seconds Seconds RFU Control Lysate RUN T - POROSITY/THICKNESS, VMF4 DRYER TEMP, LINESPEED 1 NA NA NA NA NA NA NA NA NA NA NA NA NA 1 NA NA NA NA NA NA NA NA NA NA NA NA NA 1 NA NA NA NA NA NA NA NA NA NA NA NA NA 1 R01 Y Y Y Y Y 2.4/5.6  3.4/6.2  3.1/6.2 3.0/6.0  N/Avail. N/Avail. ≧NC 1 R02 Y Y Y Y Y 2.9/12.6 3.2/11.4 2.9/2.9 3.0/9.0  N/Avail. N/Avail. ≧NC 2 R03 Y Y Y Y Y 1.1/24.1 1.4/10.8 1.1/4.1 1.2/13.0 N/Avail. N/Avail. ≧NC 2 R04 Y Y Y Y Y 1.2/14.5 1.5/19.9 1.3/5.6 1.3/13.3 N/Avail. N/Avail. ≧NC 2 R05 Y Y Y Y Y 1.3/10.5 1.5/15.4 1.3/4.2 1.4/10.0 N/Avail. N/Avail. ≧NC 2 R06 Y Y Y Y Y 1.3/24.7 1.4/9.5  1.3/4.0 1.3/12.7 N/Avail. N/Avail. ≧NC 2 R07 Y Y Y Y Y 2.5/60.0 2.3/25.4 2.5/5.4 2.4/30.0 N/Avail. N/Avail. ≧NC 2 R08 Y Y Y Y Y 2.1/9.7  2.6/14.0 2.6/5.5 2.8/9.7  N/Avail. N/Avail. ≧NC 2 R09 Y Y Y Y Y 2.8/13.1 3.5/22.6 2.5/5.9 2.9/13.9 N/Avail. N/Avail. ≧NC 2 R10 Y Y Y Y Y 3.1/28.7 3.5/15.7 2.5/7.1 3.0/17.2 N/Avail. N/Avail. ≧NC 3 R11 Y Y Y Y Y 24.1 6.5 4.2 11.6 N/Avail. N/Avail. ≧NC 3 R12 Y Y Y Y Y 47.1 35.7 8.6 30.5 N/Avail. N/Avail. ≧NC 3 R13 Y Y Y Y Y 67.9 70.7 34.5 57.7 N/Avail. N/Avail. ≧NC 3 R14 Y Y Y N (HIGH) N (White) >180 >180 >180 >180 N/Avail. N/Avail. ≧NC 3 R15 Y Y Y N (HIGH) N (White) >180 >180 >180 >180 N/Avail. N/Avail. ≧NC 3 R16 Y Y Y N (HIGH) Y >180 57.3 16.4 >180 N/Avail. N/Avail. ≧NC 3 R17 Y Y Y Y Y 19.3 40.8 5.1 21.7 N/Avail. N/Avail. ≧NC 3 NA NA NA NA NA NA NA NA NA NA NA NA NA Segment 1 Diagnostic Segment 2 Dryer Temperature & Linespeed Variation Segment 3 Porosity and Thickness Variation - Starting Membrane

EXAMPLE 3

The protocol used for Western blotting and chemiluminescent detection is as follows:

-   -   Protein samples are electrophoretically separated using Bis:Tris         (4˜12%) midi gradient gel (Invitrogen, WG1402BOX).     -   Samples are electro-blotted at 45V for 1 hr 15 min using BioRad         tank transfer apparatus (Criterion Blotter #165-6024) onto a         hydrophilic membrane prepared as in Example 1.     -   Blots are washed 2× (3 min each) in TBS-T (0.1% Tween)     -   Blots are blocked for 1 hr at RT in TBS-T with 3% NFM (non-fat         milk, Carnation).     -   Blots are washed 2× (3 min each) in TBS-T (0.1% Tween)     -   Blots are incubated with primary antibody in TBS-T for 1 hr.     -   Blots are washed 3× (5 min each) in TBS-T (0.1% Tween)     -   Blots are incubated with secondary antibody in TBS-T for 1 hr     -   Blots are washed 4× (5 min each) in TBS-T (0.1% Tween)     -   Protein bands are visualized using ECL (Millipore Immobilon-HRP)         and x-ray film.

This protocol was used on the samples prepared in Example 2, and the blotting results are shown in FIGS. 1, 2, and 3.

Western blotting results from a typical development run demonstrate the performance differences between the hydrophilic PVDF blotting membrane of this invention, and the controls (FL—hydrophobic PVDF membrane, and NC—Whatman/S&S BA-85 membrane). Each horizontal strip in the figure contains 5 separate Western transfer blots; three blots on hydrophilic PVDF development samples, and one blot on each of the control membranes. Each strip of 5 Western blots is the result from one electrophoresis and transfer experiment (5 gels were run in each experiment). By design, each experiment embodies identical conditions with identical quantities of protein sample (applied in 4 lanes across each gel) before electrophoresis and transfer. The results shown are the transfer blots for the detection of 2 proteins (HSP70 and GAPDH) from a complex sample mixture (lysate), applied at decreasing sample solids (concentrations), from left-to-right and corresponding to: 5 ug, 2.5 ug, 1.25 ug, 0.67 ug.

Note that in each row (the result of a single electrophoresis and electro-blotting experiment, three hydrophilic blotting membranes of the invention are compared to two control blotting membranes. One control consists of nitrocellulose blotting membrane (NC) and the other control is a hydrophobic PVDF blotting membrane (FL). In the case of each single experiment, the FL membrane demonstrates the highest signal intensity for the 4 titers of analyte protein solution, and the NC membrane demonstrates the lowest signal intensity. It can be seen, when comparing the signal strengths between NC control blotting membranes and hydrophilic PVDF blotting membranes of the invention, that at the highest analyte sample titers (left hand side of each blot), that the NC and the hydrophilic PVDF membranes exhibit similar signal strengths. However, as one progresses to lower and lower analyte sample titers (progressing from left-to-right), the signal strength falls off more rapidly for the NC membrane. This demonstrates that the hydrophilic PVDF membrane allows sample detection at lower protein concentrations than NC membrane does. 

What is claimed is:
 1. A porous membrane comprising a polymeric substrate membrane, said polymeric substrate membrane having its surface modified with a crosslinked polymeric coating comprising acrylamide of the formula H2C═CH—C(O)NH2 and methylene-bis-acrylamide, wherein said coating renders said surface hydrophilic, and wherein said surface has a protein binding capacity as measured by an IgG binding test of about 250-325 μg/cm².
 2. The porous membrane of claim 1, wherein the average total organic carbon level of said membrane is below 1.5 ug/cm², and wherein extractable monomer levels, as determined by HPLC, are below 0.02 ug/cm² for acrylamide, and below 0.15 ug/cm² for methylene-bis-acrylamide.
 3. The porous membrane of claim 1, wherein said substrate has a background fluorescence value, and wherein said modified membrane exhibits a background fluorescence of about twice that of said substrate background fluorescence value under identical measurement conditions.
 4. The porous membrane of claim 1 or 3, wherein said membrane substrate comprises polyvinylidene fluoride.
 5. The porous membrane of claim 1 or 3, wherein the ratio of acrylamide to methylene-bis-acrylamide of the monomer reactant solution is about 1:1 (mass/mass).
 6. The porous membrane of claim 1 or 3, wherein the overall monomer concentration of the acrylamide:methylene-bis-acrylamide monomer reactant solution is between 0.5% and 1.5% by mass.
 7. The porous membrane of claim 1 or 3, further comprising a photoinitiator at a level between 0.01% and 0.20%.
 8. A method for preparing a hydrophilic, low background fluorescence, high protein-binding porous membrane comprising a hydrophobic, low background fluorescence, high protein binding porous membrane substrate, and a low background fluorescence surface modification, said method comprising: providing a hydrophobic, low background fluorescence, high protein-binding porous membrane substrate; contacting surface of said porous membrane with a monomer reactant solution comprising acrylamide and methylene-bis-acrylamide of the formula H2C═CH—C(O)NH2 and a photoinitiator; removing said membrane from the reaction solution; removing excess reactant solution; polymerizing said acrylamide and methylene-bis-acrylamide reactant solution under anaerobic conditions directly onto the entire hydrophobic porous membrane surface to form a continuous hydrophilic, low background fluorescence background coating; and, drying said membrane.
 9. The method of claim 8, wherein the amounts of acrylamide and methylene-bis-acrylamide in said reaction solution are 0.50% and 0.40%, respectively.
 10. The method of claim 8, wherein the amount of the photoinitiator IRGACURE®) 2959) (2-hydroxyl-1-[4-(2-hydroxyethoxy)phenyl]-2-methyl-1-propanone (Ciba-geigy) in said reaction solution is 0.10%. 